Aluminum oxide series
Melting point: 2038 ℃ It is a good insulation material with high hardness and excellent resistance to surface grinding, corrosion, cavitation, and erosion.
TCR-821
alumina (Al₂O₃)
Al₂O₃ > 99.50
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
TCR-822
Aluminum oxide titanium (AT13) (Al₂O₃-TiO₂)
TiO₂:13.00 Al₂O₃:87.00
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
TCR-823
Aluminum oxide titanium (AT40) (Al₂O₃-TiO₂)
TiO₂:40.00 Al₂O₃:60.00
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
TCR-825
Aluminum oxide titanium (AT3) (Al₂O₃-TiO₂)
TiO₂:3.00 Al₂O₃:97.00
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
TCR-826
Aluminum oxide titanium (AT20) (Al₂O₃-TiO₂)
TiO₂:20.00 Al₂O₃:80.00
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
TCR-827
Aluminum oxide titanium (AT50) (Al₂O₃-TiO₂)
TiO₂:50.00 Al₂O₃:50.00
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
TCR-828
Silicon oxide alumina (SiO₂-Al₂O₃)
SiO₂:30.00 Al₂O₃:70.00
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
TCR-829
Magnesium oxide alumina (MgO-Al₂O₃)
MgO:28.00 Al₂O₃:72.00
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
45 - 75 µm · 15 - 45 µm · 10 - 30 µm