Chromium oxide series
Melting point: 2265 ℃ The coating is dense, with low porosity, high hardness, good polishing performance, wear-resistant particles, hard surfaces, and fiber wear, resistant to particle erosion and cavitation, and excellent corrosion resistance.
TCR-811
Pure chromium oxide (Cr₂O₃)
Cr₂O₃ > 99.50
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
TCR-812
Chromium oxide (silicon) (Cr₂O₃-TiO₂-SiO₂)
TiO₂:3.00 SiO₂:5.00 Cr₂O₃:92.00
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
TCR-813
Chromium (titanium) oxide (Cr₂O₃-TiO₂)
TiO₂:10.00 Cr₂O₃:90.00
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
TCR-815
Chromium oxide (aluminum) (Cr₂O₃-Al₂O₃)
Al₂O₃:25.00 Cr₂O₃:75.00
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
45 - 75 µm · 15 - 45 µm · 10 - 30 µm
Need a different particle size?
Ranges are adjusted to the spray system and coating specification. Send the substrate and target coating thickness.